Explore the exceptional versatility of ASTM 3003 aluminum sheet, a widely used material in various industries due to its excellent corrosion resistance and formability. Our AISI 3003 aluminum sheets are manufactured to meet stringent standards, ensuring high quality for applications such as chemical equipment, sheet stock, and 3003 H14 aluminum variants. These sheets are perfect for general fabrication and offer superior performance in 3003 O temper conditions, making them ideal for ductile uses. With options like 3003 H18 aluminum for higher strength, our products cater to diverse needs, from commercial suppliers to specialized ASTM B209 3003 compliant projects.

ASTM AISI 3003 Aluminum Alloy Sheet is a manganese-based alloy known for its good mechanical properties and weldability, making it a preferred choice in sectors requiring durability and ease of processing. This material is commonly available in various tempers and thicknesses to suit specific industrial demands.

Product Parameters

• Chemical Composition: Manganese 1.0-1.5%, Copper 0.05-0.20%, with aluminum as the remainder.
• Tensile Strength: Ranges from 110 MPa (16,000 psi) in O temper to 200 MPa (29,000 psi) in H18 temper.
• Yield Strength: Approximately 40 MPa (5,800 psi) for O temper and 186 MPa (27,000 psi) for H18 temper.
• Elongation: Up to 30% in O temper, decreasing to 10% in H18 temper.
• Density: 2.73 g/cm³, providing a lightweight solution for many applications.
• Thermal Conductivity: 193 W/m·K, ensuring efficient heat dissipation.
• Electrical Conductivity: Approximately 50% IACS, suitable for electrical components.
• Corrosion Resistance: Excellent resistance to atmospheric and chemical corrosion.